| Product Name | Mullite Castable | High Strength Mullite Castable | PA-Corundum Mullite Castable | Silicon Carbide Crusting-resistant Castable | High Performance Wear-resistant Castable | High Performance Wear-resistant Castable | High Alumina High Strength Castable |
High Strength Alkali-resistant Castable |
High Strength Explosion-proof Castable | High Abrasion-resistant Erosion-resistant Castable | Plastic repair material | |
| Model Name | M-16 | G-17M | PA-16 | GC-16 | G-16K | GF-16 | G-16 | GT-13N | SJ-16 | GS-17M | SK-15 | |
| Chemical composition | Al2O3+SiC% | ≥60 | ≥63 | ≥68 | ≥65 | ≥60 | ≥58 | ≥55 | ≥50 | ≥50 | ≥50 | ≥60 |
| Density(g/cm³) | 110ºC×24h | ≥2.40 | ≥2.50 | ≥2.60 | ≥2.50 | ≥2.50 | ≥2.50 | ≥2.50 | ≥2.40 | ≥2.60 | ≥2.60 | ≥2.60 |
| Modulus of Rupture (MPa) | 110ºC×24h | ≥70 | ≥80 | ≥80 | ≥60 | ≥60 | ≥70 | ≥60 | ≥70 | ≥60 | ≥70 | ≥70 |
| 1100ºC×3h | ≥100 | ≥100 | ≥105 | ≥80 | ≥80 | ≥90 | ≥70 | ≥90 | ≥80 | ≥100 | ≥70 | |
| Cold Crushing Strength (MPa) | 110ºC×24h | ≥8 | ≥10 | ≥10 | ≥8 | ≥10 | ≥10 | ≥8 | ≥10 | ≥10 | ≥8 | ≥7 |
| 1100ºC×3h | ≥10 | ≥10 | ≥10 | ≥10 | ≥10 | ≥12 | ≥10 | ≥10 | ≥10 | ≥10 | ≥8 | |
| Permanent Linear Change (%) | 1100ºC×3h | ±0.3 | ±0.2 | ±0.2 | ±0.2 | ±0.3 | ±0.3 | ±03 | ±0.3 | ±0.3 | ±0.3 | ±3 |
| Product Name | New Tabular Corundum Alumina Castable |
High Performance Castable for Kiln Outlet | Castable for Kiln Outlet | New Tabular Corundum Alumina (Burner Pipe) Castable |
Castable for Burner Pipe | Corundum Wear-resistant Castable | |
| Model Name | GB-18 | GY-18 | SY-18 | GR-18 | SR-17 | GP-16 | |
| Chemical composition | Al2O3+SiC% | 70 | 65 | 60 | 75 | 65 | 58 |
| Density(g/cm³) | 110ºC×24h | 2.80 | 2.70 | 2.70 | 2.80 | 2.70 | 2.70 |
| Modulus of Rupture (MPa) | 110ºC×24h | ≥90 | ≥80 | ≥80 | ≥90 | ≥80 | ≥80 |
| 1100ºC×3h | ≥110 | ≥100 | ≥100 | ≥110 | ≥100 | ≥100 | |
| 1400ºC×3h | ≥110 | ≥110 | ≥100 | ≥110 | ≥100 | ≥100 | |
| Cold Crushing Strength (MPa)) | 110ºC×24h | ≥10 | ≥8 | ≥8 | ≥10 | ≥8 | ≥8 |
| 1100ºC×3h | ≥10 | ≥10 | ≥10 | ≥10 | ≥10 | ≥10 | |
| 1400ºC×3h | ≥11 | ≥10 | ≥10 | ≥11 | ≥10 | ≥10 | |
| Permanent Linear Change (%) | 1100ºC×3h | ±0.2 | ±0.2 | ±0.3 | ±0.2 | ±0.3 | ±0.2 |
| 1400ºC×3h | ±0.3 | ±0.3 | ±0.3 | ±0.3 | ±0.3 | ±0.3 | |